METALES Y PLÁSTICOS TÉCNICOS

PLÁSTICOS

CARACTERISTICAS TECNICAS

MATERIAL DENSIDAD
gr/cm3
PUNTO
FUSION
ºC
TEMP.
MAXIMA
UTIL. CONT.
ºC
TEMP.
MINIMA
UTIL. CONT.
ºC
ALARG. A
ROTURA
%
RESIST. A
ROTURA
Kg / cm2
NYLON
PA – 6
1,14 213 90 -40 >50 650
POLIAMIDA
PA – 66
1,15 250 110 -30 25 700
POLIAMIDA
PA - 6 G
1,15 220 105 -40 25  
POLIAMIDA
PA-6G+MoS2
1,15 210 100 -30 >50  
POLIAMIDA
PA - 6 PLAC
1,13 220 100 -20 >10  
POLIAMIDA
PA – 66+6GF30
1,29 255 120 -20 7  
POM 1,41 165 100 -50 400 600
PET 1,38 250 100 -20 15 750
TEFLON
PTFE
2,2 327 260 -250 250 a 400 200 a 300
PVC 1,4 110 60 -10 150 550
POLIPROPILENO
PP
0,91 160 100 -10 650 300
POLIETILENO
PE-300
0,95 135 80   >800  
POLIETILENO
PE-500
0,96 135 80 -100 >600 300
POLIETILENO
PE-1000
0,94 135 80 -250 >450 250
PEEK 1,32 343 260   25  
METACRILATO
PMMA
1,18   70 -100 10  
POLICARBONATO
PC
1,2 150 120 -100 >100 650
POLIURETANO
PU
1,25     -20 530  

 

MATERIAL RESIST. AL
CHOQUE
Kj / m2
MODULO
ELAST.
TRACCION
N / mm2
ABSORCION
AGUA
100% Hr 23
%
RESIST.
SUPERF.
OHM
CONDUC.
TERMICA
W / Km
DUREZA
Shore D.A.
Rockwell M.
Brinell H.
NYLON
PA – 6
3,8 2800 9 5.1012 0,28 D.75
POLIAMIDA
PA – 66
5 3000 8 1.1013 0,25 D.75
POLIAMIDA
PA - 6 G
4 3300 6,5 1.1013 0,29 M.88
POLIAMIDA
PA-6G+MoS2
    6     M.90
POLIAMIDA
PA - 6 PLAC
4 2800 6,5     M.80
POLIAMIDA
PA – 66+6GF30
  5200 5,5 1.1013 0,3 M.98
POM 7 2900 0,8 1.1013 0,31 M.90
PET 4 3400 0,6 6.1014 0,29 M.95
TEFLON
PTFE
16 750 0 1.1018 0,25 D.65-85
PVC 12 3000 0,1 1.1013 0,2 D.73
POLIPROPILENO
PP
NO ROMPE 1300 0,01 1.1013 0,22 D.65
POLIETILENO
PE-300
NO ROMPE 1000 0,01 1.1013 0,43 D.65
POLIETILENO
PE-500
NO ROMPE 900 0,01 1.1013 0,42 D.65
POLIETILENO
PE-1000
NO ROMPE 700 0,01 1.1013 0,42 D.50
PEEK   3000 0,1 1015   D.65
METACRILATO
PMMA
18 3300 0,3 1015 0,19 H.190
POLICARBONATO
PC
>30 2300 0,35 1.1016 0,21 M.75
POLIURETANO
PU
          D.90